Outdoor expansion type steel structure fireproof coating

Brand:BAOHANG
model:Ultra thin type (without particles)、Thin particles
Certification certificate:Three system certificates, SGS certification
country of origin:China

Categories:

Contact Now
colour Expansion ratio Minimum order quantity EXW price FOB price payment method Supply capacity period for dispatch Packaging form Packaging size
Customizable Micro expansion 6 tons 320 USD/ton 412 USD/ton T/T,L/C,D/P,D/D,Paypal 60 60 tons/day Delivery within 3 days upon receipt of payment 25kg/barrel 31cm*31cm*36cm
5 times 2 tons 1250 USD/ton 1530 USD/ton
10 times 2 tons 1668 USD/ton 1945 USD/ton
Micro expansion 6 tons 292 USD/ton 385 USD/ton
5 times 2 tons 1210 USD/ton 1488 USD/ton
10 times 2 tons 1668 USD/ton 1945 USD/ton
Note: Fireproof coating requires approximately 1kg of 1mm thickness to be sprayed per square meter.

Product Introduction:

The outdoor expansion type steel structure fireproof coating is suitable for the fire protection of the surface of various steel structure engineering load-bearing components, and the implementation standard is GB14907-2018. It is a similar product to the outdoor thin and ultra-thin steel structure fireproof coating that complies with the GB14907-2002 standard. This coating is made by adding various fireproof components to a polymer base material. The product has the characteristics of salt spray resistance, corrosion resistance, freeze-thaw resistance, acid and alkali resistance, etc. When subjected to fire or high temperature attacks, fireproof coatings will form a dense fireproof barrier, hindering the penetration of heat into the substrate, preventing or suppressing combustion, and providing fireproof protection for the substrate. Fireproof coatings have the characteristics of thin coating, long-lasting weather resistance, and easy application operation. Suitable for fire protection of various outdoor building heavy-duty steel structural components in aerospace, petroleum, chemical, power, metallurgy, national defense, light defense industry, etc. It is also particularly suitable for steel structural engineering with fire hazards of hydrocarbon chemicals (such as oils, solvents, etc.), such as fire protection of petrochemical engineering, automobile depots, oil drilling platforms, oil storage facility support frames, etc. Water based or solvent based (i.e. water-based or oil-based) can be selected according to regulatory requirements. Our company has a professional construction team with superb skills and attentive service. Convenient construction: spray coating, roller coating, brush coating are all available. 1.Strong adhesion: It has strong adhesion to epoxy, alkyd, and phenolic anti rust primers 2.Durable and sturdy 3.Widely applicable, of high quality and low cost

The models are divided into:

GT-WRP-Fp2.00-BH01 GT-WSP-Ft2.00-HBBH GT-WSP-Ft1.50-HBBH GT-WSP-Ft1.00-HBBH

Performance indicators:

The state in the container Drying time (surface drying) Initial drying crack resistance Adhesive strength Heat resistance Freeze thaw cycle resistance Acid and alkali resistance
After stirring, it is in a uniform and delicate state or a thick fluid state, without clumping. ≤12h No cracks should appear ≥0.15MPa After 720 hours of testing, the coating should have no delamination, peeling, hollowing, or cracking, and the insulation efficiency attenuation should be ≤ 35% After 15 tests, the coating should have no cracking, peeling, or foaming, and the insulation efficiency attenuation should be ≤ 35% After 360 hours of testing, the coating should have no delamination, peeling, or cracking, and the insulation efficiency attenuation should be ≤ 35%

Fire resistance time:

Fire resistance time Fp2.0h Ft2.0h Ft1.5h Ft1.0h
Coating thickness 2.38mm 4.5mm 3.5mm 2.5mm

Construction method:

1. Before construction, rust removal and rust prevention treatment should be carried out on the surface of the steel, and surface oil stains and dust should be removed. 2. The solid content of the coating is relatively high, so it is necessary to stir the coating evenly before use. For the convenience of construction, it can be diluted with water or solvent. 3. The construction of outdoor expansion type steel structure fireproof coating can adopt various methods such as brushing, roller coating, and airless spraying. 4. Construction should be carried out at a temperature above 5 ℃, and both manual painting and mechanical spraying can be used. The thickness of each layer of construction should not exceed 0.5mm. The next painting can only be carried out after the coating surface is dry, until the specified thickness is reached. 5. Construction should not be carried out when there is condensation on the surface of the component or when the air humidity exceeds 90%. The applied coating should not be exposed to rain before it is fixed. Unused paint should be resealed for future use.

Packaging and Transportation:

1. The outdoor expansion type steel structure fireproof coating is packaged in iron or plastic drums. 2. The storage and transportation temperature should be above 0-35 ℃, and should not be stored outdoors or exposed to sunlight. 3. The effective storage period of the product is 6-12 months. 4. During transportation, measures should be taken to prevent rain, exposure to sunlight, freezing, and impact, and relevant regulations of the transportation department should be followed.

Product List

Contact Us

  • Hebei Baohang Fireproof Materials Co., Ltd
    • +86 18032602060admin@baohangfireproof.com
  • Da Mengqiao Village, Dacheng County, Langfang City, Hebei Province, China

    • Request Inquery

    Products

    Request a Quote

    News

    Contact Us

  • Hebei Baohang Fireproof Materials Co., Ltd
    • +86 18032602060admin@baohangfireproof.com
  • Damengqiao Village, Dacheng County, Langfang City, Hebei Province, China

    • Copyright © 2024 Hebei Baohang Fireproof Materials Co., Ltd All Rights Reserved.Privacy Policy

    Contact Us

    Request Inquery