طلاء مقاوم للحريق للأنفاق

العلامة التجارية: باوهانج
الموديل: أساس أسمنتي
شهادة الاعتماد: ثلاث شهادات نظام، شهادة SGS
بلد المنشأ: الصين

فئات:سلسلة طلاء مقاومة للحريق

اتصل الآن

وصف

لون	الحد الأدنى لكمية الطلب	سعر EXW	سعر فوب	طريقة الدفع	القدرة على التوريد	فترة للإرسال	نموذج التعبئة والتغليف	حجم العبوة
رمادي	10 طن	140 دولار أمريكي/طن	195 دولار/طن	T / T، L / C، D / P، D / D، باي بال	100 طن / يوم	التسليم خلال 3 أيام من استلام الدفع	25 كجم/كيس	75 سم * 40 سم * 10 سم

ملاحظة: يتطلب الطلاء المقاوم للحريق رش حوالي 1 كجم بسماكة 1 مم لكل متر مربع.

مقدمة المنتج:

SH-SD-103 tunnel fireproof coating is mainly composed of inorganic fireproof insulation materials, and it is applied to the concrete surface of highway tunnels, railway tunnels, and building floors. Due to its low coating density and thermal conductivity, it effectively improves the fire resistance limit of concrete structures. Provided reliable fire protection for the tunnel. At the same time, its coating density is low and porous, which has a significant sound-absorbing effect when applied in tunnels. Has the following characteristics: 1. Environmentally friendly products that are non-toxic and harmless to human health and the environment. 2. Strong adhesion, no cracking or detachment. 3. Easy to construct, can be manually applied or mechanically sprayed. 4. Thin coating thickness, good fire resistance, and long fire resistance limit. 5. Good water and moisture resistance, diverse colors. 6. It has significant sound absorption and noise reduction effects on long curved tunnels. Suitable for walls inside highways, provincial highways, and national highway tunnels, mainly used for fire prevention of tunnel walls. The fire protection effect is better and has an ideal anti-corrosion effect. In general, the application of anti rust paint can be omitted and directly applied. SH-SD-103 tunnel fireproof coating is developed by the China Fire Protection Research Institute. After years of practical development and improvement, the formula has gradually been perfected. The coating forms a thick and dense fire insulation layer in case of fire, with remarkable fire resistance, and has excellent physical and chemical properties such as fast drying, moisture resistance, freeze-thaw resistance, corrosion resistance, aging resistance, etc Its coating is thin and the surface is flat, with good decorative effect, suitable for fire protection of various walls, especially concrete walls.

مؤشرات الأداء:

رقم سري	اسم عنصر التفتيش	المتطلبات القياسية
1	الدولة في الحاوية	بعد التحريك، يصبح في حالة سائلة موحدة وسميكة دون أي تكتل.
2	وقت التجفيف (التجفيف السطحي)، ح	≥24 ساعة
3	قوة السندات	≥0.15MPa، (قبل ذوبان الجليد والتجميد)
3	قوة السندات	≥0.15MPa، (بعد ذوبان التجميد)
4	الكثافة الجافة	≥700 (كجم/م³)
5	مقاومة الأحماض والقلويات	≥ 360 ساعة، بعد الاختبار، لا يتشقق الطلاء أو يتقشر أو يتقشر. السماح بتورم طفيف وتغير اللون
6	أداء مقاومة الحريق	≥2.00 (التدفئة القياسية)
		≥2.00 (ارتفاع درجة حرارة HC)
		التدفئة ≥ 1.50، التبريد ≥ 1.83 (تسخين RABT)

طريقة البناء:

1. Construction equipment: sand coating mixer, extrusion grouting pump, air compressor, painting, cleaning, transportation tools, etc. 2. Construction preparation: (1) Set up scaffolding (2) Electricity and water supply (3) Remove floating dust and oil stains on the surface of tunnel concrete, and wet it with water (4) The uneven surface should be repaired, and the particularly smooth concrete surface should be plastered with mortar (5) The leaking area needs to be repaired for waterproofing. 3. Base surface treatment A. The oil stains left on the surface during the demolding process of tunnel lining should be thoroughly cleaned by the tunnel construction unit with diesel or specialized degreaser; B. Before spraying construction, it is necessary to remove the floating dust on the surface of the structure, mainly targeting the areas with severe dust accumulation within a height range of 2 meters on both sides of the wall; C. 24 hours before spraying construction, rinse the overall base interface with clean water to remove floating ash, dust, and dirt on the surface. D. Considering that the construction joint of the tunnel is a concentrated point of "stress deformation", the common quality problem of hollowing and cracking of the fireproof coating is often caused by untimely and incomplete cutting of the fireproof coating construction joint. Based on similar engineering practice, it is recommended to apply the concrete special interface agent produced by Huili Company within 30CM on both sides of the construction joint after rinsing the base interface with clean water during construction to enhance the bonding strength between the coating and the base. 4. Tunnel fireproof coating application According to the technical requirements of the standard GB28375-2012 Fire resistant Coating for Concrete Structures, with a fire resistance limit of ≥ 2.0 hours, spraying construction is adopted, and it is considered to be sprayed in four layers. The construction design of fire-resistant coatings for urban tunnel passages takes into account the impact of vibrations from vehicles, trains, and other sources. To improve the bonding strength and overall integrity of the coating, a reinforcement (mesh) treatment scheme is usually adopted. A. Construction of pasting insulation nails and hanging nets: Use mixed glue to paste insulation nails on the surface of concrete. The construction spacing of insulation nails is about 25cm, and the steel wire mesh should be laid flat. The specification and size of the steel wire mesh should be 0.6mm/1 inch, and the construction requirements are that the steel wire mesh should be laid flat, without bulging or rebounding. B. Surface Primer (1st coat): This coating is mixed with a special adhesive to form a primer, with a ratio of 3:1:2 (weight ratio) of coating: special adhesive: water. The mixture is stirred in a low-speed mixer for 5-8 minutes and left to stand for 5 minutes (preferably with uniform material mixing). Then, the coating is sent to an extrusion equipment for spraying, and the spraying thickness should not exceed 3mm. In response to issues such as bulging and rebounding of local steel wire mesh after primer spraying, technical measures such as flattening, cutting and trimming should be taken to ensure that the steel wire mesh is flat and does not expose the bottom. C. Mid coat spraying (2nd to 3rd coat): After the surface of the base material is dry, it can be applied. The surface coating ratio is 1:1 (weight ratio) of paint to water. The mixture is stirred in a low-speed mixer for 5-8 minutes and left to stand for about 5 minutes (preferably with uniform material mixing). Then, the paint is sent to an extrusion equipment for spraying. During construction, spraying should be carried out in two batches, with each batch having a thickness controlled between 6-8mm. D. Surface coating spraying (4th layer): The surface coating ratio is the same as the intermediate coating. At the same time, to ensure the overall coating thickness, uniformity, and appearance, during the surface coating fireproof coating spraying construction, the spray gun diameter and pressure are adjusted to control the flatness of the coating and the height difference between particles should not exceed 3mm, so as to make the coating appear as a uniform granular surface and enhance the sound absorption effect of the tunnel structure. (3) Tunnel fireproof coating decorative topcoat coating After the fireproof coating is basically dry and formed (usually with a construction interval of about 7 days), the surface decorative topcoat can be applied. The decorative topcoat material is "acrylic emulsion paint" produced by Shanghai Huili Company. When using, a suitable amount of water can be added and diluted according to the construction method. After stirring evenly, it can be used. Rolling, brushing, and spraying methods can be used for construction. It is recommended to use an airless spraying machine for spraying, and the spraying should have a uniform color and no obvious color difference. (Note: The paint color sample shall be based on the color chart provided by our Huili Company or the national standard color card.) Construction precautions： (1) The mixed material should be used up within 30 minutes. The construction temperature should be above 5 ℃, and the wind speed should not exceed 5 meters per second. (2) During construction, the next layer can only be applied after the first layer has dried (approximately 6 hours). The spraying time interval for the second layer (surface layer) can be appropriately increased, preferably (24-48 hours) (3) After the construction is completed, try to avoid strong vibrations and hard impacts within two weeks to ensure the quality of the coating. (4) In hot and dry weather, it is necessary to humidify and maintain the surface of the coating. The maintenance period is 15 days.

التعبئة والتغليف والنقل:

1. This product is packaged in woven bags lined with plastic bags, with each bag weighing 25kg. 2. This product should be stored in a cool and dry warehouse, with an effective storage period of 6 months. 3. This product is a non flammable, non explosive, non-toxic, and non corrosive safety product. During storage and transportation, pay attention to sealing to prevent moisture and rainwater from entering. Materials will become ineffective if they become damp. 4. During transportation, measures should be taken to prevent rain, exposure to sunlight, and snagging, and relevant regulations of the transportation department should be followed.

قائمة المنتجات

اتصل بنا

المنتجات ذات الصلة

منتجات

طلب عرض أسعار

أخبار

اتصل بنا

بريد إلكتروني

اتصل بنا

واتس اب